Metallized Polypropylene/CPP Film Laminated Material
-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Shandong
-
Validity to:
Long-term effective
-
Last update:
2017-12-22 01:12
-
Browse the number:
101
+
Shandong Changyu New Metallizing Materials Co., Ltd.
- Contactaixin:
Miss Laura(Mr.)
- Email: telephone:
-
Arrea:
Shandong
Address:Economical Development Zone, Dongping County, Tai'an, Shandong, China 271500
- Website:
+
VMCPP CPP Metallized film
1)Good obstructive ability
2)Superior gas and moisture barrier properties
3)Strong adhesion and evenness of the Alu layer
4)Excellent Vapor and oxygen lock
5)Low heat seal temperature and high strength of heat seal
Package usage:
The film is used as the inner layer of the composition films for packing, such as for fried food, biscuits, puffing food, etc.
Products feature:
1.Good stiffness and metallic appearance.
2.Low temperature-sealing performance.
3.Good obstruction feature.
Thickness: 20,25,30,40μm etc
Width: ≤2500 mm
Paper Core: 76mm(3″),152mm(6″)
Properity: 1.Certain barrier performance; 2.Good heat-sealable property ; 3.preferable adhesion of the aluminized layer 4.Good extension and flexility property.
Plastic Packaging Materials for printing and packaging (food grade)
Smooth End Face
Thickness Uniformity
Non-Crack
No-Crystal Point
Well Composite Performance
Clean Transport Vehicles ,Non-Pollution
Aluminium layer Well
Packaging Details:
1.bubble film, to protect from collision during transportation
2.specified label, factory label or customized label without factory information
3.different types of packing ways according to roll size or customer's request
4.wooden pallet with or without fumigation
Test Item | Test Method | Unit | Standard | Test Results | ||
Tension Strength | MD | GB/T 1040.3 | MPa | ≥120 | 136 | |
TD | ≥200 | 262 | ||||
Elongation Break | MD | GB/T 1040.3 | % | ≥180 | 165 | |
TD | ≥65 | 59 | ||||
Aluminum layer thickness | GB/T15717-1995 | Ω/ | ≤3 | 1.98 | ||
Heat Sealing Strength | QB/T2358 | ºC,N/15mm | ≥8 | 115ºC(8.6N) | ||
Haze |
GB/T2410 | % | ≤5.5 | 1.04 | ||
Friction coefficient | Static | GB/T 10006 | / | / | / | |
Dynamic | / | ≤0.80 | 0.4 | |||
Aluminum layer evenness | GB/T15717-1995 | % | ±13 | -8.82~10.72 | ||
Moirture-vapor Transmission Rate | GB/T 1037 | g/(m2·24h) | ≤2.5 | 1.12 | ||
Oxygen Transmission Rate | GB/T 19789 | cm3/(m2·24h·0.1MPa) | / | 72.56 |